Butadiene Rubber

The BR family of polybutadiene rubber helps optimize tire compositions, improving grip, fuel economy, and overall lifetime. They provide a great balance between processability and performance.

Buna® CB 24 Neodymium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 44 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Buna® CB 25 Neodymium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 44 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Buna® Nd 22 EZ Easy Processing Nd-BR (Buna Nd)
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 63 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Buna® Nd 24 EZ Easy Processing Nd-BR (Buna Nd)
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 44 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %

Chloroprene Rubber

Chloroprene rubber (international ASTM/DIN-abbreviation: CR) is a high-performance material with a wide variety of applications. Baypren® is the brand-name of the ARLANXEO range of polymers based on 2-chloro-1,3-butadiene (chloroprene), which are manufactured by water-based emulsion polymerization....

Baypren® 114 M 62 Precrosslinked Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 62 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Ash Content ≤ 1,0 wt % ISO 247 / ASTM D 5667

Ethylene Propylene Diene Rubber

EPDM is typically used in outdoor applications and at elevated temperatures of up to 150 °C. It's used in both automotive and industrial applications such as automotive sealing systems, coolant hoses, windshield wipers, oil additives, roof sheeting, window gaskets, conveyor belts, as well as wire...

Keltan® 2650 Low Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 25 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 53 wt % ASTM D 3900
ENB Content 6,0 wt % ASTM D 6047
Keltan® 6950
Regional
High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 65 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 48 wt % ASTM D 3900
ENB Content 9,0 wt % ASTM D 6047
Keltan® 6950C High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 65 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 44 wt % ASTM D 3900
ENB Content 9,0 wt % ASTM D 6047
Keltan® Eco 6950 High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 65 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 48 wt % ASTM D 3900
ENB Content 9,0 wt % ASTM D 6047

Ethylene Vinyl Acetate Rubber

ARLANXEO’s EVM rubbers are sold under the tradenames Baymod® L, Levamelt® and Levapren®. EVM rubbers are produced by copolymerization of ethylene and vinyl acetate. Our ethylene-vinyl acetate copolymers are used as synthetic rubbers, or as modifiers in thermoplastics, specifically PVC. The main...

Levapren® 600 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 60 wt % Internal Method LP 015
Levapren® 700 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 70 wt % Internal Method LP 015
Levapren® 800 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 28 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 80 wt % Internal Method LP 015
Levapren® 900 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 38 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 90 wt % Internal Method LP 015

Hydrogenated Nitrile Butadiene Rubber

ARLANXEO's HNBR product, under the Therban brand, offers excellent properties for engine components. The polarity of HNBR is directly influenced by the ACN content. Higher ACN reduces the polymer's polarity in non-polar media like oil, grease, fat, and fuels. HNBR combines excellent oil resistance...

Therban® 3627 Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 66 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 36,0 wt % ISO 24698-1
Residual Double Bonds 2,0 % IR Spectroscopy