Therban® 3406
Fully Saturated (suitable for peroxide crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
63 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® 3406 SF
Fully Saturated (suitable for peroxide crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
63 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® 3407
Fully Saturated (suitable for peroxide crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
70 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® 3446
Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
61 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
3,95 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® 3467
Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
68 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
5,5 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® 3496
Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
55 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
18,0 % |
IR Spectroscopy |
|
|
Density |
0,96 g/cm3 |
Internal Method |
|
|
|
Therban® 3607
Fully Saturated (suitable for peroxide crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
66 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
36,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® 3627
Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
66 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
36,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
2,0 % |
IR Spectroscopy |
|
|
Density |
0,96 g/cm3 |
Internal Method |
|
|
|
Therban® 3629
Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
87 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
36,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
2,0 % |
IR Spectroscopy |
|
|
Density |
0,96 g/cm3 |
Internal Method |
|
|
|
Therban® 3907
Fully Saturated (suitable for peroxide crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
70 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
39,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,96 g/cm3 |
Internal Method |
|
|
|
Therban® 4307
Fully Saturated (suitable for peroxide crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
63 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
42,5 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,98 g/cm3 |
Internal Method |
|
|
|
Therban® 4309
Fully Saturated (suitable for peroxide crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
100 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
43,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,98 g/cm3 |
Internal Method |
|
|
|
Therban® 4367
Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
61 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
43,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
5,5 % |
IR Spectroscopy |
|
|
Density |
0,98 g/cm3 |
Internal Method |
|
|
|
Therban® 4369
Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
97 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
43,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
5,5 % |
IR Spectroscopy |
|
|
Density |
0,98 g/cm3 |
Internal Method |
|
|
|
Therban® AT 3404
Low Mooney – Advanced Technology Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
39 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® AT 3443
Low Mooney – Advanced Technology Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
39 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
34,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
4,0 % |
IR Spectroscopy |
|
|
Density |
0,95 g/cm3 |
Internal Method |
|
|
|
Therban® AT 3904
Low Mooney – Advanced Technology Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
39 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
39,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,96 g/cm3 |
Internal Method |
|
|
|
Therban® AT 4364
Low Mooney – Advanced Technology Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
39 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
43,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
5,5 % |
IR Spectroscopy |
|
|
Density |
0,98 g/cm3 |
Internal Method |
|
|
|
Therban® LT 2007
Low Temperature Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
74 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
21,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
0,9 % |
IR Spectroscopy |
|
|
Density |
0,96 g/cm3 |
Internal Method |
|
|
|
Therban® LT 2157
Low Temperature Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
70 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
21,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
5,5 % |
IR Spectroscopy |
|
|
Density |
0,96 g/cm3 |
Internal Method |
|
|
|
Therban® XT VP
Special Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
77 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698-1 |
|
|
Residual Double Bonds |
3,5 % |
IR Spectroscopy |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|