Baypren® 110 M 41
M-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
41 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 110 M 49
M-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
49 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 110 M 65
M-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
65 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 114 M 62
Precrosslinked Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
62 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 116 M 45
XD-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
45 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 126 M 70
XD-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
70 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 210 M 43
M-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
43 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 210 M 48
M-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
48 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 211 M 39
M-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
39 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 213-1
Medium Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
150 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 213-2
Medium Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
300 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 214 M 55
Precrosslinked Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
55 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 215 M 50
Precrosslinked Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
50 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 216 M 43
XD-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
43 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 216 M 49
XD-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
49 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 223-2
Medium Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
680 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
100 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 230 M 108
M-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
108 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 233-1
Medium Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
850 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 233-2
Medium Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
1.150 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 243-2
Medium Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
2.100 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 253-2
Medium Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
3.900 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 310-1
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
150 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 320-1
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
450 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 320-2
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
680 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 321-1
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
450 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 330-1
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
850 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 330-2
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
1.150 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 340-2
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
2.100 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 350-2
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
3.900 mPa.s |
Internal Method |
10% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 360 VP
Fast Crystallizing Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Solution Viscosity |
330 mPa.s |
Internal Method |
5% in Toluene |
23 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 510 M 42
Sulfur-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
42 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 510 M 50
Sulfur-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
42 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 611 M 43
Sulfur-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
43 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 611 M 48
Sulfur-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
48 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 616 VP
Sulfur-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
43 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|
Baypren® 711 M 48
Sulfur-modified Grades
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
48 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,23 g/cm3 |
Internal Method |
|
|
|