EMULSION-STYRENE BUTADIENE RUBBERS (E-SBR)

E-SBR is predominantly used for the production of car tires, light truck tires and truck tire retread compounds. It presents good mechanical properties, abrasion, and tear resistance.

Filter by:
Buna® SE 1500 Oil-free E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 52 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1502 H Oil-free E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 53 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1502 L Oil-free E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 49 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1783 Oil-extended E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 49 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Oil Content 27,2 wt % ASTM D 5774
Buna® SE 1793 Oil-extended E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 51 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Oil Content 27,2 wt % ASTM D 5774
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1799 Oil-extended E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 40,0 wt % ASTM D 5775
Oil Content 27,2 wt % ASTM D 5774
Density 0,94 g/cm3 ASTM D 297
Taktene® Latex S62 Latex
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 135 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Brookfield Viscosity 800 cps ASTM D1417 25 °C
Bound Styrene 24,0 wt % ASTM D 5775
Total Solids 68,0 wt % ASTM D 1417
Superficial Tension 33,5 dyn/cm ASTM D 1417