X_Butyl® BB 2030
Bromobutyl Rubber
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
32 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Bromine Content |
1,80 wt % |
Internal Method |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
< 0,7 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
< 0,7 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
X_Butyl® BB 2040
Bromobutyl Rubber
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
39 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Bromine Content |
1,80 wt % |
Internal Method |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
≤ 0,7 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
≤ 0,7 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
X_Butyl® BB X2
Bromobutyl Rubber
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
46 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Bromine Content |
1,80 wt % |
Internal Method |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
≤ 0,7 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
≤ 0,7 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
X_Butyl® CB 1240
Chlorobutyl Rubber
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
38 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Chlorine Content |
1,25 wt % |
Internal Method |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
≤ 0,5 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
≤ 0,5 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
32 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Bromine Content |
1,80 wt % |
Internal Method |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
< 0,7 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
< 0,7 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
46 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Bromine Content |
1,80 wt % |
Internal Method |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
< 0,7 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
< 0,7 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
51 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
< 0,3 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
< 0,3 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
33 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
< 0,3 wt % |
ISO 247 / ASTM D 5667 |
|
|
|
X_Butyl® RB 101-3
Regular Butyl Rubber
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
51 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Unsaturation |
1,75 %(Mol) |
(*) |
|
|
Ash Content |
≤ 0,3 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
≤ 1 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
X_Butyl® RB 301
Regular Butyl Rubber
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
51 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Unsaturation |
1,85 %(Mol) |
(*) |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
≤ 0,3 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
≤ 0,3 wt % |
ISO 248 / ASTM D 5668 |
|
|
|
X_Butyl® RB 402
Regular Butyl Rubber
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
33 MU |
ISO 289 / ASTM D 1646 |
ML (1+8) |
125 °C |
Unsaturation |
2,25 %(Mol) |
(*) |
|
|
Antioxidant non-staining |
> 0,03 wt % |
Internal Method |
|
|
Ash Content |
≤ 0,3 wt % |
ISO 247 / ASTM D 5667 |
|
|
Volatile Content |
≤ 0,3 wt % |
ISO 248 / ASTM D 5668 |
|
|
|