Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
48 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
27,5 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
65 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
28,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
110 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
30 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
30 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
44 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
45 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
45 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
70 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
50 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
43,5 wt % |
ISO 24698 |
|
|
Density |
1,00 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
55 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
48,5 wt % |
ISO 24698 |
|
|
Density |
1,00 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
75 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
48,5 wt % |
ISO 24698 |
|
|
Density |
1,00 g/cm3 |
Internal Method |
|
|
|
Krynac® M 3340 F
Plasticizer Extended
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
33 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33 wt % |
ISO 24698 |
|
|
Density |
0,98 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
78 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Density |
1,06 g/cm3 |
Internal Method |
|
|
|
Krynac® X 146
Carboxylated
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
45 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
32,5 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
Krynac® X 160
Carboxylated
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
58 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
32,5 wt % |
ISO 24698 |
|
|
Density |
0,97 g/cm3 |
Internal Method |
|
|
|
Krynac® X 740
Carboxylated
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
38 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
26,5 wt % |
ISO 24698 |
|
|
Density |
0,99 g/cm3 |
Internal Method |
|
|
|
Krynac® X 750
Carboxylated
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
47 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
27,0 wt % |
ISO 24698 |
|
|
Density |
0,99 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
47 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Chlorine Content |
< 0,1 wt % |
Internal Method |
|
|
Acrylonitrile Content |
27,0 wt % |
ISO 24698 |
|
|
Density |
0,99 g/cm3 |
Internal Method |
|
|
|
Krynac® XL 3355
Pre-Crosslinked
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
55 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
1,00 g/cm3 |
Internal Method |
|
|
|
|
Property |
Nominal Value |
Test Method |
Condition |
Temperature |
Mooney Viscosity |
75 MU |
ISO 289 / ASTM D 1646 |
ML (1+4) |
100 °C |
Acrylonitrile Content |
33,0 wt % |
ISO 24698 |
|
|
Density |
1,00 g/cm3 |
Internal Method |
|
|
|