Regular Butyl & Halogenated Butyl Rubber

Butyl rubber (IIR) is a synthetic rubber, a copolymer of isobutylene with isoprene. Providing excellent air retention, it is widely used for tire inner liners among other applications.

Filter by:
X_Butyl® BB 2030 Bromobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 32 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Bromine Content 1,80 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content < 0,7 wt % ISO 247 / ASTM D 5667
Volatile Content < 0,7 wt % ISO 248 / ASTM D 5668
X_Butyl® BB 2040 Bromobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 39 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Bromine Content 1,80 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,7 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,7 wt % ISO 248 / ASTM D 5668
X_Butyl® BB X2 Bromobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 46 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Bromine Content 1,80 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,7 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,7 wt % ISO 248 / ASTM D 5668
X_Butyl® CB 1240 Chlorobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 38 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Chlorine Content 1,25 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,5 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,5 wt % ISO 248 / ASTM D 5668
X_Butyl® RB 301 Regular Butyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 51 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Unsaturation 1,85 %(Mol) (*)
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,3 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,3 wt % ISO 248 / ASTM D 5668
X_Butyl® RB 402 Regular Butyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 33 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Unsaturation 2,25 %(Mol) (*)
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,3 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,3 wt % ISO 248 / ASTM D 5668

BUTADIENE RUBBERS (BR)

The BR family of polybutadiene rubber helps optimize tire compositions, improving grip, fuel economy, and overall lifetime. They provide a great balance between processability and performance.

Filter by:
Buna® CB 1203 Cobalt BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 43 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Density 0,91 g/cm3 ASTM D 297
Buna® CB 1220 Cobalt BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 40 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 % Internal Method
Density 0,91 g/cm3 ASTM D 297
Buna® CB 1221 Cobalt BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 53 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Density 0,91 g/cm3 ASTM D 297
Buna® CB 22 Neodymium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 63 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Density 0,91 g/cm3 ASTM D 297
Buna® CB 24 Neodymium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 44 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Density 0,91 g/cm3 ASTM D 297
Buna® CB 25 Neodymium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 44 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content > 96 %
Density 0,91 g/cm3 ASTM D 297
Buna® CB 45 Lithium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 45 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content 38 %
Density 0,90 g/cm3 ASTM D 297
Buna® CB 45 VP Lithium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 45 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content 38 %
Density 0,90 g/cm3 ASTM D 297
Buna® CB 55 NF Lithium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content 38 %
Density 0,90 g/cm3 ASTM D 297
Buna® CB 60 Lithium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 60 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Cis 1,4 Content 38 %
Density 0,90 g/cm3 ASTM D 297
Load more

Chloroprene Rubber

Chloroprene rubber (international ASTM/DIN-abbreviation: CR) is a high-performance material with a wide variety of applications. Baypren® is the brand-name of the ARLANXEO range of polymers based on 2-chloro-1,3-butadiene (chloroprene), which are manufactured by water-based emulsion polymerization....

Filter by:
Baypren® 213-1 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 150 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 213-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 300 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 223-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 680 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 233-1 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 850 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 233-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 1.150 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 243-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 2.100 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 253-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 3.900 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 310-1 Fast Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 150 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 320-1 Fast Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 450 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 320-2 Fast Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 680 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Load more

EMULSION-STYRENE BUTADIENE RUBBERS (E-SBR)

E-SBR is predominantly used for the production of car tires, light truck tires and truck tire retread compounds. It presents good mechanical properties, abrasion, and tear resistance.

Filter by:
Buna® SE 1502 H Oil-free E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 53 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1502 L Oil-free E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 49 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1793 Oil-extended E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 51 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Oil Content 27,2 wt % ASTM D 5774
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1799 Oil-extended E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 40,0 wt % ASTM D 5775
Oil Content 27,2 wt % ASTM D 5774
Density 0,94 g/cm3 ASTM D 297

Ethylene Propylene Diene Rubber

EPDM is typically used in outdoor applications and at elevated temperatures of up to 150 °C. It's used in both automotive and industrial applications such as automotive sealing systems, coolant hoses, windshield wipers, oil additives, roof sheeting, window gaskets, conveyor belts, as well as wire...

Filter by:
Keltan® 3250
Regional
Low Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 33 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution Narrow Internal Method
Ethylene Content 55 wt % ASTM D 3900
ENB Content 2,3 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 3960 Low Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 35 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution Medium Internal Method
Ethylene Content 56 wt % ASTM D 3900
ENB Content 11,0 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 4869C Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 48 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 62 wt % ASTM D 3900
ENB Content 8,7 wt % ASTM D 6047
Oil Content 100 PHR ISO 1407
Density 0,88 g/cm3 Internal Method
Keltan® 6950C High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 65 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 44 wt % ASTM D 3900
ENB Content 9,0 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 8570C High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 80 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 66 wt % ASTM D 3900
ENB Content 5,0 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 9950C Very high Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 60 MU ISO 289 / ASTM D 1646 ML (1+8) 150 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 44 wt % ASTM D 3900
ENB Content 9,0 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® Eco-BC 6950C High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 65 MU ISO 289 / ASTM D 1646 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 44 wt % ASTM D 3900
ENB Content 9,0 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method

Ethylene Vinyl Acetate Rubber

ARLANXEO’s EVM rubbers are sold under the tradenames Baymod® L, Levamelt® and Levapren®. EVM rubbers are produced by copolymerization of ethylene and vinyl acetate. Our ethylene-vinyl acetate copolymers are used as synthetic rubbers, or as modifiers in thermoplastics, specifically PVC. The main...

Filter by:
Baymod® L 2450 Thermoplast Modification Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 3 g/10mi ASTM D 1238
Vinyl Acetate Content 45 wt % Internal Method LP 015
Density 0,99 g/cm3 Internal Method
Particle Size 620 µm DIN EN ISO 4610
Separating Agent ≤ 0.8 wt % 7 wt % DIN EN 14582
Levamelt® 450 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 3 g/10mi ISO 1133
Vinyl Acetate Content 45 wt % Internal Method LP 015
Density 0,99 g/cm3 Internal Method
Levamelt® 456 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 25 g/10mi ISO 1133
Vinyl Acetate Content 45 wt % Internal Method LP 015
Density 0,99 g/cm3 Internal Method
Levamelt® 600 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 2,75 g/10mi ISO 1133
Vinyl Acetate Content 60 wt % Internal Method LP 015
Density 1,04 g/cm3 Internal Method
Levamelt® 686 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 25 g/10mi ISO 1133
Vinyl Acetate Content 68 wt % Internal Method LP 015
Density 1,06 g/cm3 Internal Method
Levapren® 450 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 20 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 45 wt % Internal Method LP 015
Density 0,99 g/cm3 Internal Method
Levapren® 600 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 60 wt % Internal Method LP 015
Density 1,04 g/cm3 Internal Method
Levapren® 700 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 70 wt % Internal Method LP 015
Density 1,07 g/cm3 Internal Method

Nitrile Butadiene Rubber

Nitrile-butadiene rubber (NBR) is a copolymer made from butadiene and acrylonitrile. NBR is essential for technical rubber products that need to be resistant to mineral oils, service fluids, and greases in automotive applications and machinery.

Perbunan® 3481 F Fast Cure Clean
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 78 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 34,7 wt % ISO 24698
Density 0,97 g/cm3 Internal Method

SOLUTION-STYRENE BUTADIENE RUBBERS (S-SBR)

The tire industry is the main market segment for S-SBR. S-SBR offers improved wet grip and reduced rolling resistance — which translate to greater safety and better fuel economy.

Filter by:
Buna® FX 3234A-2 Functionalized S-SBR (Buna FX)
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 65 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Styrene Content 34 wt % Internal Method
Oil Content 27,3 wt % Internal Method
Vinyl Content 32 wt % Internal Method
Density 0,95 g/cm3 ASTM D 297
Buna® VSL 3038-2 HM Standard S-SBR (Buna VSL)
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 66 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Styrene Content 38 wt % Internal Method
Oil Content 27,3 wt % Internal Method
Vinyl Content 30 wt % Internal Method
Density 0,96 g/cm3 ASTM D 297
Buna® VSL 4526-2 Standard S-SBR (Buna VSL)
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 50 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Styrene Content 26 wt % Internal Method
Oil Content 27,3 wt % Internal Method
Vinyl Content 44,5 wt % Internal Method
Density 0,94 g/cm3 ASTM D 297
Buna® VSL 4526-2 HM Standard S-SBR (Buna VSL)
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 62 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Styrene Content 26 wt % Internal Method
Oil Content 27,3 wt % Internal Method
Vinyl Content 44,5 wt % Internal Method
Density 0,94 g/cm3 ASTM D 297