Ethylene Vinyl Acetate Rubber

ARLANXEO’s EVM rubbers are sold under the tradenames Baymod® L, Levamelt® and Levapren®. EVM rubbers are produced by copolymerization of ethylene and vinyl acetate. Our ethylene-vinyl acetate copolymers are used as synthetic rubbers, or as modifiers in thermoplastics, specifically PVC. The main...

Baymod® L 2450 Thermoplast Modification Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 3 g/10mi ASTM D 1238
Vinyl Acetate Content 45 wt % Internal Method LP 015
Density 0,99 g/cm³ Internal Method
Particle Size 620 µm DIN EN ISO 4610
Separating Agent ≤ 0.8 wt % 7 wt % ISO 247 / ASTM D 5667
Baymod® L 6515 VP Thermoplast Modification Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 4 g/10mi ASTM D 1238
Vinyl Acetate Content 65 wt % Internal Method LP 015
Density 1,05 g/cm³ Internal Method
Particle Size 750 µm DIN EN ISO 4610
Separating Agent ≤ 0.8 wt % 15 wt % ISO 247 / ASTM D 5667
Levamelt® 600 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 2,75 g/10mi ISO 1133
Vinyl Acetate Content 60 wt % Internal Method LP 015
Density 1,04 g/cm³ Internal Method
Levamelt® 686 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 25 g/10mi ISO 1133
Vinyl Acetate Content 68 wt % Internal Method LP 015
Density 1,06 g/cm³ Internal Method
Levapren® 400 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 20 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 40 wt % Internal Method LP 015
Density 0,98 g/cm³ Internal Method
Levapren® 600 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 60 wt % Internal Method LP 015
Density 1,04 g/cm³ Internal Method
Levapren® NPG VP Special Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 20 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 60 wt % Internal Method LP 015
Density 1,04 g/cm³ Internal Method