Regular Butyl & Halogenated Butyl Rubber

Butyl rubber (IIR) is a synthetic rubber, a copolymer of isobutylene with isoprene. Providing excellent air retention, it is widely used for tire inner liners among other applications.

X_Butyl® BB 2030 Bromobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 32 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Bromine Content 1,80 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content < 0,7 wt % ISO 247 / ASTM D 5667
Volatile Content < 0,7 wt % ISO 248 / ASTM D 5668
X_Butyl® BB 2040 Bromobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 39 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Bromine Content 1,80 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,7 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,7 wt % ISO 248 / ASTM D 5668
X_Butyl® BB X2 Bromobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 46 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Bromine Content 1,80 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,7 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,7 wt % ISO 248 / ASTM D 5668
X_Butyl® CB 1240 Chlorobutyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 38 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Chlorine Content 1,25 wt % Internal Method
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,5 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,5 wt % ISO 248 / ASTM D 5668
X_Butyl® RB 301 Regular Butyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 51 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Unsaturation 1,85 %(Mol) (*)
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,3 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,3 wt % ISO 248 / ASTM D 5668
X_Butyl® RB 402 Regular Butyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 33 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Unsaturation 2,25 %(Mol) (*)
Antioxidant non-staining > 0,03 wt % Internal Method
Ash Content ≤ 0,3 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,3 wt % ISO 248 / ASTM D 5668

EMULSION-STYRENE BUTADIENE RUBBERS (E-SBR)

E-SBR is predominantly used for the production of car tires, light truck tires and truck tire retread compounds. It presents good mechanical properties, abrasion, and tear resistance.

Buna® SE 1502 H Oil-free E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 53 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Density 0,94 g/cm3 ASTM D 297
Buna® SE 1502 L Oil-free E-SBR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 49 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Bound Styrene 23,5 wt % ASTM D 5775
Density 0,94 g/cm3 ASTM D 297

Ethylene Propylene Diene Rubber

EPDM is typically used in outdoor applications and at elevated temperatures of up to 150 °C. It's used in both automotive and industrial applications such as automotive sealing systems, coolant hoses, windshield wipers, oil additives, roof sheeting, window gaskets, conveyor belts, as well as wire...

Keltan ® 13951C DE Very high Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 92 MU ISO 289 / ASTM D 1646 ML (1+8) 150 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 44 wt % ASTM D 3900
ENB Content 9,0 wt % ASTM D 6047
Oil Content 15 PHR ISO 1407
Density 0,86 g/cm3
Keltan® 13561C Very high Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 92 MU ISO 289 / ASTM D 1646 ML (1+8) 150 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 56 wt % ASTM D 3900
ENB Content 5,5 wt % ASTM D 6047
Oil Content 15 PHR ISO 1407
Density 0,86 g/cm3 Internal Method