Ethylene Propylene Diene Rubber

EPDM is typically used in outdoor applications and at elevated temperatures of up to 150 °C. It's used in both automotive and industrial applications such as automotive sealing systems, coolant hoses, windshield wipers, oil additives, roof sheeting, window gaskets, conveyor belts, as well as wire...

Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 80 MU ISO 289 / ASTM D 1646 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 48 wt % ASTM D 3900
ENB Content 5,5 wt % ASTM D 6047
Density 0,86 g/cm³ Internal Method
Keltan® 10675C Very high Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 67 MU ISO 289 / ASTM D 1646 ML (1+8) 150 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 65 wt % ASTM D 3900
ENB Content 6,0 wt % ASTM D 6047
Oil Content 50 PHR ISO 1407
Density 0,87 g/cm³ Internal Method
Keltan® 4465 Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 48 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution Broad Internal Method
Ethylene Content 56 wt % ASTM D 3900
ENB Content 4,1 wt % ASTM D 6047
Oil Content 50 PHR ISO 1407
Density 0,87 g/cm³ Internal Method
Keltan® 4577 Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 46 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution Narrow Internal Method
Ethylene Content 66 wt % ASTM D 3900
ENB Content 5,1 wt % ASTM D 6047
Oil Content 75 PHR ISO 1407
Density 0,88 g/cm³ Internal Method
Keltan® 4869C Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 48 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 62 wt % ASTM D 3900
ENB Content 8,7 wt % ASTM D 6047
Oil Content 100 PHR ISO 1407
Density 0,88 g/cm³ Internal Method
Keltan® 5465 Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 37 MU ISO 289 / ASTM D 1646 ML (1+8) 150 °C
Molecular Weight Distribution Narrow Internal Method
Ethylene Content 64 wt % ASTM D 3900
ENB Content 4,0 wt % ASTM D 6047
Oil Content 50 PHR ISO 1407
Density 0,87 g/cm³ Internal Method
Keltan® 5467C Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 52 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 58 wt % ASTM D 3900
ENB Content 4,5 wt % ASTM D 6047
Oil Content 75 PHR ISO 1407
Density 0,88 g/cm³ Internal Method
Keltan® 5469C Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 52 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 58 wt % ASTM D 3900
ENB Content 4,5 wt % ASTM D 6047
Oil Content 100 PHR ISO 1407
Density 0,88 g/cm³ Internal Method
Keltan® 6160D High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 63 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution Medium Internal Method
Ethylene Content 64 wt % ASTM D 3900
DCPD Content 1,2 wt % ASTM D 6047
Density 0,86 g/cm³ Internal Method
Keltan® 8550C High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 80 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 48 wt % ASTM D 3900
ENB Content 5,5 wt % ASTM D 6047
Density 0,86 g/cm³ Internal Method

Hydrogenated Nitrile Butadiene Rubber

ARLANXEO's HNBR products, summarized under the Therban® brand, offer excellent properties wherever high temperature and fluid resistance is needed. The polarity of HNBR is directly influenced by the ACN content. Higher ACN increases the polymer's polarity and, therefore, resistance in non-polar...

Therban® 4367 Partially Saturated (suitable for peroxide and sulfur crosslinking) Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 61 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 43,0 wt % ISO 24698-1
Residual Double Bonds 5,5 % IR Spectroscopy
Density 0,98 g/cm³ Internal Method
Therban® LT 2007 Low Temperature Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 74 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 21,0 wt % ISO 24698-1
Residual Double Bonds 0,9 % IR Spectroscopy
Density 0,96 g/cm³ Internal Method