Chloroprene Rubber

Chloroprene rubber (international ASTM/DIN-abbreviation: CR) is a high-performance material with a wide variety of applications. Baypren® is the brand-name of the ARLANXEO range of polymers based on 2-chloro-1,3-butadiene (chloroprene), which are manufactured by water-based emulsion polymerization....

Filter by:
Baypren® 213-1 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 150 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 213-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 300 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 223-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 680 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 233-1 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 850 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 233-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 1.150 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 243-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 2.100 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 253-2 Medium Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 3.900 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 310-1 Fast Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 150 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 320-1 Fast Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 450 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method
Baypren® 320-2 Fast Crystallizing Grades
Property Nominal Value Test Method Condition Temperature
Solution Viscosity 680 mPa.s Internal Method 10% in Toluene 23 °C
Density 1,23 g/cm3 Internal Method