Chloroprene Rubber

Chloroprene rubber (international ASTM/DIN-abbreviation: CR) is a high-performance material with a wide variety of applications. Baypren® is the brand-name of the ARLANXEO range of polymers based on 2-chloro-1,3-butadiene (chloroprene), which are manufactured by water-based emulsion polymerization....

Filter by:
Baypren® 116 M 45 XD-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 45 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method
Baypren® 210 M 43 M-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 43 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method
Baypren® 210 M 48 M-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 48 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method
Baypren® 211 M 39 M-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 39 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method
Baypren® 214 M 55 Precrosslinked Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method
Baypren® 215 M 50 Precrosslinked Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 50 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method
Baypren® 216 M 43 XD-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 43 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method
Baypren® 216 M 49 XD-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 49 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm³ Internal Method