Baypren® 110 M 41
Mmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
41 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 


Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
49 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 


Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
65 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 112 M 41
Mmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
41 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 114 M 62
Precrosslinked Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
62 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 116 M 43
XDmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
43 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 116 M 49
XDmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
49 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 126 M 70
XDmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
70 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 210 M 43
Mmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
43 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 210 M 48
Mmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
48 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 211 M 39
Mmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
39 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 2131
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
150 mPa.s 
Internal Method 



Baypren® 2132
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
300 mPa.s 
Internal Method 



Baypren® 214 M 55
Precrosslinked Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
55 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 215 M 50
Precrosslinked Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
50 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 216 M 43
XDmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
43 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 216 M 49
XDmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
49 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 2232
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
680 mPa.s 
Internal Method 




Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
100 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 230 M 108
Mmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
108 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 2331
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
850 mPa.s 
Internal Method 



Baypren® 2332
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
1.150 mPa.s 
Internal Method 



Baypren® 2432
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
2.100 mPa.s 
Internal Method 



Baypren® 2531
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
2.800 mPa.s 
Internal Method 



Baypren® 2532
Medium Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
3.900 mPa.s 
Internal Method 



Baypren® 3101
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
150 mPa.s 
Internal Method 



Baypren® 3201
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
450 mPa.s 
Internal Method 



Baypren® 3202
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
680 mPa.s 
Internal Method 



Baypren® 3211
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
450 mPa.s 
Internal Method 



Baypren® 3301
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
850 mPa.s 
Internal Method 



Baypren® 3302
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
1.150 mPa.s 
Internal Method 



Baypren® 3402
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
2.100 mPa.s 
Internal Method 



Baypren® 3501
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
2.800 mPa.s 
Internal Method 



Baypren® 3502
Fast Crystallizing Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Solution Viscosity 
3.900 mPa.s 
Internal Method 



Baypren® 510 M 42
Sulfurmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
42 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 510 M 50
Sulfurmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
50 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 611 M 43
Sulfurmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
43 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 611 M 48
Sulfurmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
43 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 711 M 43
Sulfurmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
43 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 

Baypren® 711 M 48
Sulfurmodified Grades

Property 
Nominal Value 
Test Method 
Condition 
Temperature 
Mooney Viscosity 
48 MU 
ISO 289 / ASTM D 1646 
ML (1+4) 
100 °C 